Loctite® Fixmaster® 98743 2-Part Wear Resistant Putty, 3 lb Kit, Part A: Paste; Part B: Solid, Paste
Loctite® Fixmaster® Wear Resistant Putty, 2-Part, Series: PC 7222, Kit, 3 lb, Epoxy Base, Composition: Part A: Aluminum Oxide, Diethylenetriamine, Alkyl Phenol, Silicon Dioxide, Epoxy Polyamine Adduct, 4,4'-Isopropylidenediphenol, Triethylenetetramine, Substituted Piperazine, Titanium Dioxide, Aluminum, Alkyl Phenol, Benzyl Alcohol, Benzyldimethylamine ; Part B: Silicon Carbide, Epoxy Resin, Aluminum Oxide, Treated Fumed Silica, Cristobalite, Carbon Black, Aluminum, Part A: Paste; Part B: Solid, Paste, 342 sq-cm at 6 mm Thk/0.45 kg Coverage, 30 min Application, 6 hr Curing, Part A: Dark Gray, Part B: Gray, Part A: Ammoniacal, Part B: Slight, Epoxy, -30 to 105 deg C, Part A: 1.07, Part B: 2.228 Specific Gravity, Part A : > 93 deg C, Part B: 250 deg C Flash, 2:1 By Volume/2:1 By Weight Mixing, Applicable Materials: Aluminum, Brass, Concrete, Iron, Plastic, Steel, Wood, 3020 psi Tensile, 2440 psi Shear Strength
- Ceramic fibers that give this trowelable putty excellent wear and abrasion resistant properties under typical dry service temperatures of -29 to 107 deg C
- Provides smooth, low friction finish for equipment exposed to wear, erosion, and cavitation
- Renews worn surfaces fast reduces downtime
- Small ceramic bead filled resists fine particle sliding abrasion, prolongs equipment life
- D 89 shore hardness
- 45 to 55 gel time at 25 deg C
- Epoxy hardener part A, epoxy resin part B